Kaiweite® S50C SAE1050 High carbon steel plate for mold base is suitable for making small cross-section quenching and tempering parts under load and large normalizing parts with high-stress, as well as surface hardened parts with low requirements on the strength of the core, such as tips, guide posts, hands and other parts.Quenched and subsequently tempered steel for screws, forgings, wheel tyres, shafts, sickles, axes, knives, woodworking drills, hammers, etc.
1. Product Introduction
Kaiweite® S50C SAE1050 High carbon steel plate for mold base is suitable for making small cross-section quenching and tempering parts under load and large normalizing parts with high-stress, as well as surface hardened parts with low requirements on the strength of the core, such as tips, guide posts, hands and other parts.Quenched and subsequently tempered steel for screws, forgings, wheel tyres, shafts, sickles, axes, knives, woodworking drills, hammers, etc.
We believe that long expression partnership is often a result of top of the range, value added service, prosperous encounter and personal contact for Online Exporter China Kaiweite® S50C SAE1050 High carbon steel plate for mold base, Remember to come to feel absolutely free to speak to us for organization. nd we believe we are going to share the most beneficial trading practical experience with all our merchants.
High Quality Online Exporter China S50C SAE1050 High carbon steel plate for mold base , High Strength Steel Sheets, We taking advantage of experience workmanship, scientific administration and advanced equipment, ensure the product quality of production, we not only win the customers' faith, but also build up our brand. Today, our team is committed to innovation, and enlightenment and fusion with constant practice and outstanding wisdom and philosophy, we cater to the market demand for high-end products, to do specialist solutions.
2. Product Parameter (Specification)
|
Place of Origin: |
ningbo, China |
|
Application: |
Ship Plate |
|
Standard: |
AiSi, ASTM, bs, DIN, GB, JIS |
|
Width: |
2000-2300mm |
|
Length: |
2000-5800mm/3000-5800mm |
|
Grade: |
Carbon steel plate |
|
Tolerance: |
±10% |
|
Processing Service: |
Bending, Welding, Decoiling, Cutting, Punching |
|
Product Name: |
c50 1050 s50c 1.1210 steel |
|
MOQ: |
1Ton |
|
Shape: |
Round bars/steel sheets |
|
Certificate: |
ISO Certificate |
|
Technology: |
Hot Rolled/ Forged |
|
Keyword: |
s50c 1050 c50 1.1210 |
|
Experience: |
25 years manufacture experience |
|
Type: |
Steel Plate, Steel Plate |
|
Technique: |
Hot Rolled/Forged |
|
Surface Treatment: |
Black/Bright |
3. Product Feature And Application
1.Chemical composition(%)
|
C |
Si |
Mn |
P |
S |
Cr |
Ni |
|
0.47 - 0.55 |
0.17- 0.37 |
0.50 - 0.80 |
≤0.035 |
≤0.035 |
≤ 0.25 |
≤ 0.30 |
2. Equivalent Steel Grade
|
GB |
ASTM |
JIS |
|
50 |
1050 |
S50C |
3.Surface Treatment
Plate: Origin Black, Orign cold rolled bright, Machined, Grinded Round Bar: Origin Black, Orign cold rolled(drawn) bright, Turned, Peeled, Grinded
4.Characteristic
Medium-carbon high-strength carbon structural steel with high strength and hardness after quenching, the steel has mediummachinability, low cold deformation plasticity, poor weldability, no temper brittleness during heat treatment, but lowhardenability, and critical diameter in water 13 * 30mm, and there is a tendency to crack during water quenching. This steel isusually used after heat treatment such as normalizing or quenching and tempering, or high-frequency surface quenching.
5.Mechanical properties
Tensile strength σb (MPa): ≥630 (64)
Yield strength σs (MPa): ≥375 (38)
Elongation δ5 (%): ≥14
Section shrinkage ψ (%): ≥40
Impact energy Akv (J): ≥31 (4)
Impact strength value αkv (J/cm²): ≥39 (4)
Hardness: unheated, ≤241HB; annealed steel, ≤207HB
4. Product Details
5.Deliver,Shipping And Serving
20-25 working days
Shipping depend on customer, by sea and by train
Wooden box packaging